Factory For Super C2 Welding Rod - Stainless Steel Welding Electrode AWS E308-16 (A102) – Tianqiao

Short Description:


Product Detail

Product Category

Product Tags

Related Video

Feedback (2)

Dedicated to strict high-quality management and considerate shopper company, our experienced team associates are normally available to discuss your requirements and ensure full shopper gratification for 309l Stainless Steel , Cheap Welding Rods , Atlas Welding Rod , With superb service and quality, and an enterprise of foreign trade featuring validity and competitiveness, that will be trusted and welcomed by its clients and creates happiness to its employees.
Factory For Super C2 Welding Rod - Stainless Steel Welding Electrode AWS E308-16 (A102) – Tianqiao Detail:

APPLICATIONS:

It can be used to the corrosion resistance of stainless steel structure, such as the 06Cr19Ni9 and 06Cr19Ni11Ti, whose working temperature below 300 ℃; it can also be used for stainless steel structure using under cryogenic temperatures, such as liquid nitrogen container, liquefied natural gas containers, etc.

CHARACTERISTICS:

E308-16 is a coated rutile type Cr18Ni9 stainless steel. Both AC and DC can be used and can be all-position welding. It can reach excellent welding performance, stable arc, little spatter, easy slag removal and good weld appearance. The deposited metal has good resistance to inter granular corrosion.

ATTENTION:

1. The electrodes must be baked by 320-350 ℃ for 1 hour before welding, dry the electrode when use it.

2. The rust, oil, water and other impurities of the weld must be removed before welding.

3.Recommended DC power supply, because AC welding has a shallow penetration, the current should not be too large, in order to avoid the coating redness and cracking.

4. To minimize the amount of heat input and welding electrode oscillating amplitude should not be too big.

5. Preheat and interlayer-temperature should remain below 150 ℃

WELDING POSITIONS:

PA, PB, PD, PF

DEPOSIT COMPOSITION (Quality Score):  %

items

C

Cr

Ni

Mo

Mn

Si

P

S

Cu

Requirements

≤0.08

18.0-21.0

9.0-11.0

≤0.75

0.5-2.5

≤1.00

≤0.04

≤0.03

≤0.75

Typical Results

0.062

19.34

10.14

0.28

1.08

0.66

0.025

0.010

0.08

MECHANICAL PROPERTIES:

items

Tensile Strength

Rm/MPa

Elongation A/%

Charpy V-Notch

KV2(J)-196℃

Requirements

≥550

≥30

≥29

Typical Results

570

38

36

TYPICAL OPERATING PROCEDURES: (AC, DC+)

Diameter (mm)

2.0

2.5

3.2

4.0

5.0

Current (A)

25-50

50-80

80-110

110-160

160-200

PACKAGING:

5kg/box, 4boxes/carton, 20kgs/carton, 50cartons/pallet. 21MT -26MT per 1X20″ FCL.

OEM/ODM:

We support OEM/ODM and could make packaging accord to your design, please contact us for detail discussion.

General requirements:
The manufacture of welded structural parts shall comply with the design, process documents and the provisions of this standard. 3.2 Requirements for ambient temperature during welding production:
When parts and finished products are rectified, the temperature should not be lower than the following:
Low carbon steel material: -20℃;
Low alloy structural steel material: -15℃.
Generally, the allowable welding temperature of welding parts should meet the requirements of Table.
When welding parts are welded under low temperature conditions (as listed in Table 1), the surface of the steel should be preheated. The width of the preheating zone must be greater than 4 times the thickness of the plate to be welded, and the preheating width on each side must not be less than 100mm. Welding can only be done after heating to 100~~200℃. If flame preheating is used, the distance between the flame core and the board surface should be greater than 50mm.
Under normal temperature conditions, for welding parts with high rigidity and poor weldability, preheating should also be carried out before welding (the preheating temperature is within the range of 100~200℃), and heat preservation or tempering should be carried out after welding to eliminate welding stress.

 


Product detail pictures:

Factory For Super C2 Welding Rod -  Stainless Steel Welding Electrode AWS E308-16 (A102) – Tianqiao detail pictures

Factory For Super C2 Welding Rod -  Stainless Steel Welding Electrode AWS E308-16 (A102) – Tianqiao detail pictures

Factory For Super C2 Welding Rod -  Stainless Steel Welding Electrode AWS E308-16 (A102) – Tianqiao detail pictures


Related Product Guide:
The composition of the welding electrode

Our primary target will be to provide our clients a serious and responsible small business relationship, supplying personalized attention to all of them for Factory For Super C2 Welding Rod - Stainless Steel Welding Electrode AWS E308-16 (A102) – Tianqiao, The product will supply to all over the world, such as: Bangkok, Brisbane, Lebanon, We look forward to hearing from you, whether you are a returning customer or a new one. We hope you will find what you are looking for here, if not, please contact us immediately. We pride ourselves on top notch customer service and response. Thank you for your business and support!

  • We have been engaged in this industry for many years, we appreciate the work attitude and production capacity of the company, this is a reputable and professional manufacturer.
    5 Stars By Nicole from Jordan - 2017.12.02 14:11
    The factory technical staff gave us a lot of good advice in the cooperation process, this is very good, we are very grateful.
    5 Stars By Doris from Mauritius - 2017.07.28 15:46

    Send your message to us:

    Write your message here and send it to us

    Related Products

    Send your message to us: