To be able to give you benefit and enlarge our business, we also have inspectors in QC Team and assure you our greatest service and products for 7018 Ac , Welding Electrode E6010 , Dissimilar Metal Welding Electrodes , We've been not pleased while using the present achievements but we are trying finest to innovate to satisfy buyer's much more personalized needs. No matter where you will be from, we have been here to wait for your sort ask for, and welcom to go to our manufacturing facility. Choose us, you can meet your trusted supplier.
Factory source Tungsten Rod 2.4 Mm - Z308  Pure nickel cast iron electrode GB / T 10044 EZNi-1 AWS ENi-C1 JIS DFCNi – Tianqiao Detail:

APPLICATIONS:

It is suitable for the welding of thin pieces of cast iron welding and machining surfaces, such as cylinder heads, important gray cast iron engine blocks, gear boxes, and Machine Tool and soon.

CHARACTERISTICS:

THZ308 is pure nickel welding core, strong reduction of graphite type coating iron rod. It can be used in AC and DC dual purpose and is  easy to operate. When welding, it is not necessary for weldment to preheat. It has good crack resistance and processability.

RECAUTIONS:

1. Before welding, the electrodes need to be baked for 1 hour with the temperature of 150±10℃ before using.
2 It can eliminate welding stress and avoid crack by hammering the welding seam.
3. In order to reduce the impurity elements in the base metal penetration weld, narrow white band width, improve crack resistance and processing properties, it should use small current welding in cast iron cold welding.

Chemical Composition of the deposited metal(the mass fraction): %  

Elements

C

Si

Mn

S

Fe

Ni

The mass of other elements

Standard value

≤2.0

≤2.5

≤1.0

≤0.03

≤8.0

≥90

≤1.0

Welding reference current: (AC,DC+)

Electrode diameter(mm)

2.5

3.2

4.0

Welding current(A)

60-90

90-110

120-150

Welding distortion correction:

For deformation correction in hot state, mechanical correction and hammering are strictly prohibited in the range of blue brittle temperature (300℃~500℃) to avoid brittle cracks.

Pay attention to the following requirements when the flame is locally heated

It is not advisable to repeat heating at the same part to avoid changes in the metallographic structure and mechanical properties of the steel.

Do not cause repeated corrections of tension and compression in the same part.

For hardenable welded parts, watering and rapid cooling are strictly prohibited.

Welding parts that need to be annealed should be rectified before annealing to eliminate internal stress during annealing. During annealing, the welded parts must be placed steadily so as not to deform again.

The flame straightening heating temperature can be 700℃~850℃ (fuchsia), and should not exceed 900℃ (bright red) for low alloy structural steel.


Product detail pictures:

Factory source Tungsten Rod 2.4 Mm - Z308  Pure nickel cast iron electrode  GB / T 10044 EZNi-1 AWS ENi-C1    JIS DFCNi – Tianqiao detail pictures

Factory source Tungsten Rod 2.4 Mm - Z308  Pure nickel cast iron electrode  GB / T 10044 EZNi-1 AWS ENi-C1    JIS DFCNi – Tianqiao detail pictures

Factory source Tungsten Rod 2.4 Mm - Z308  Pure nickel cast iron electrode  GB / T 10044 EZNi-1 AWS ENi-C1    JIS DFCNi – Tianqiao detail pictures

Factory source Tungsten Rod 2.4 Mm - Z308  Pure nickel cast iron electrode  GB / T 10044 EZNi-1 AWS ENi-C1    JIS DFCNi – Tianqiao detail pictures


Related Product Guide:
The composition of the welding electrode

We've been committed to offering easy,time-saving and money-saving one-stop purchasing support of consumer for Factory source Tungsten Rod 2.4 Mm - Z308  Pure nickel cast iron electrode GB / T 10044 EZNi-1 AWS ENi-C1 JIS DFCNi – Tianqiao, The product will supply to all over the world, such as: Suriname, Netherlands, Kenya, We provide good quality but unbeatable low price and the best service. Welcome to post your samples and color ring to us .We will produce the goods according to your request. If you are interested in any products we offer, please feel free to contact us directly by mail, fax, telephone or internet. We are here to answer your questions from Monday to Saturday and looking forward to cooperating with you.

  • We always believe that the details decides the company's product quality, in this respect, the company conform our requirements and the goods are meet our expectations.
    5 Stars By Julia from Belize - 2017.12.19 11:10
    We are long-term partners, there is no disappointment every time, we hope to maintain this friendship later!
    5 Stars By Flora from Washington - 2018.10.01 14:14

    Send your message to us:

    Write your message here and send it to us

    Related Products

    Send your message to us: