Good quality 309 Electrode - Z308 Pure nickel cast iron electrode GB / T 10044 EZNi-1 AWS ENi-C1 JIS DFCNi – Tianqiao

Short Description:

Product Detail

Product Category

Product Tags

Feedback (2)

As a way to provide you advantage and enlarge our organization, we even have inspectors in QC Crew and guarantee you our greatest assistance and product or service for Stainless Steel Filler Wire , Good 7018 Welds , Weld Metal Welding Rod , Seeing believes! We sincerely welcome the new customers abroad to set up business relationships and also expect to consolidate the relationships with the long-established customers.

Good quality 309 Electrode - Z308 Pure nickel cast iron electrode GB / T 10044 EZNi-1 AWS ENi-C1 JIS DFCNi – Tianqiao Detail:

APPLICATIONS:

It is suitable for the welding of thin pieces of cast iron welding and machining surfaces, such as cylinder heads, important gray cast iron engine blocks, gear boxes, and Machine Tool and soon.

CHARACTERISTICS:

THZ308 is pure nickel welding core, strong reduction of graphite type coating iron rod. It can be used in AC and DC dual purpose and is easy to operate. When welding, it is not necessary for weldment to preheat. It has good crack resistance and processability.

RECAUTIONS:

1. Before welding, the electrodes need to be baked for 1 hour with the temperature of 150±10℃ before using.
2 It can eliminate welding stress and avoid crack by hammering the welding seam.
3. In order to reduce the impurity elements in the base metal penetration weld, narrow white band width, improve crack resistance and processing properties, it should use small current welding in cast iron cold welding.

Chemical Composition of the deposited metal(the mass fraction): %

Elements	C	Si	Mn	S	Fe	Ni	The mass of other elements
Standard value	≤2.0	≤2.5	≤1.0	≤0.03	≤8.0	≥90	≤1.0

Welding reference current: (AC,DC⁺)

Electrode diameter(mm)	2.5	3.2	4.0
Welding current(A)	60-90	90-110	120-150

Welding distortion correction:

For deformation correction in hot state, mechanical correction and hammering are strictly prohibited in the range of blue brittle temperature (300℃~500℃) to avoid brittle cracks.

Pay attention to the following requirements when the flame is locally heated

It is not advisable to repeat heating at the same part to avoid changes in the metallographic structure and mechanical properties of the steel.

Do not cause repeated corrections of tension and compression in the same part.

For hardenable welded parts, watering and rapid cooling are strictly prohibited.

Welding parts that need to be annealed should be rectified before annealing to eliminate internal stress during annealing. During annealing, the welded parts must be placed steadily so as not to deform again.

The flame straightening heating temperature can be 700℃~850℃ (fuchsia), and should not exceed 900℃ (bright red) for low alloy structural steel.

Product detail pictures:

Related Product Guide:
The composition of the welding electrode

Our primary objective is usually to offer our shoppers a serious and responsible small business relationship, offering personalized attention to all of them for Good quality 309 Electrode - Z308 Pure nickel cast iron electrode GB / T 10044 EZNi-1 AWS ENi-C1 JIS DFCNi – Tianqiao, The product will supply to all over the world, such as: Lisbon, San Francisco, Cyprus, We have advanced production technology, and pursuit innovative in goods. At the same time, the good service has enhanced the good reputation. We believe that as long as you understand our product, you need to be willing to become partners with us. Looking forward to your inquiry.