We can constantly satisfy our respected customers with our good high quality, good price tag and good support due to we have been additional specialist and extra hard-working and do it in cost-effective way for 6011 Welding Rod 5 32 , Electrode 3.2 Mm , E70 Electrode , We have experienced manufacturing facilities with more than 100 employees. So we can guarantee short lead time and quality assurance.
High Quality for 7011 Welding Rod - Z308  Pure nickel cast iron electrode GB / T 10044 EZNi-1 AWS ENi-C1 JIS DFCNi – Tianqiao Detail:

APPLICATIONS:

It is suitable for the welding of thin pieces of cast iron welding and machining surfaces, such as cylinder heads, important gray cast iron engine blocks, gear boxes, and Machine Tool and soon.

CHARACTERISTICS:

THZ308 is pure nickel welding core, strong reduction of graphite type coating iron rod. It can be used in AC and DC dual purpose and is  easy to operate. When welding, it is not necessary for weldment to preheat. It has good crack resistance and processability.

RECAUTIONS:

1. Before welding, the electrodes need to be baked for 1 hour with the temperature of 150±10℃ before using.
2 It can eliminate welding stress and avoid crack by hammering the welding seam.
3. In order to reduce the impurity elements in the base metal penetration weld, narrow white band width, improve crack resistance and processing properties, it should use small current welding in cast iron cold welding.

Chemical Composition of the deposited metal(the mass fraction): %  

Elements

C

Si

Mn

S

Fe

Ni

The mass of other elements

Standard value

≤2.0

≤2.5

≤1.0

≤0.03

≤8.0

≥90

≤1.0

Welding reference current: (AC,DC+)

Electrode diameter(mm)

2.5

3.2

4.0

Welding current(A)

60-90

90-110

120-150

Welding distortion correction:

For deformation correction in hot state, mechanical correction and hammering are strictly prohibited in the range of blue brittle temperature (300℃~500℃) to avoid brittle cracks.

Pay attention to the following requirements when the flame is locally heated

It is not advisable to repeat heating at the same part to avoid changes in the metallographic structure and mechanical properties of the steel.

Do not cause repeated corrections of tension and compression in the same part.

For hardenable welded parts, watering and rapid cooling are strictly prohibited.

Welding parts that need to be annealed should be rectified before annealing to eliminate internal stress during annealing. During annealing, the welded parts must be placed steadily so as not to deform again.

The flame straightening heating temperature can be 700℃~850℃ (fuchsia), and should not exceed 900℃ (bright red) for low alloy structural steel.


Product detail pictures:

High Quality for 7011 Welding Rod - Z308  Pure nickel cast iron electrode  GB / T 10044 EZNi-1 AWS ENi-C1    JIS DFCNi – Tianqiao detail pictures

High Quality for 7011 Welding Rod - Z308  Pure nickel cast iron electrode  GB / T 10044 EZNi-1 AWS ENi-C1    JIS DFCNi – Tianqiao detail pictures

High Quality for 7011 Welding Rod - Z308  Pure nickel cast iron electrode  GB / T 10044 EZNi-1 AWS ENi-C1    JIS DFCNi – Tianqiao detail pictures

High Quality for 7011 Welding Rod - Z308  Pure nickel cast iron electrode  GB / T 10044 EZNi-1 AWS ENi-C1    JIS DFCNi – Tianqiao detail pictures


Related Product Guide:
The composition of the welding electrode

We intention to see quality disfigurement within the creation and supply the ideal support to domestic and overseas buyers wholeheartedly for High Quality for 7011 Welding Rod - Z308  Pure nickel cast iron electrode GB / T 10044 EZNi-1 AWS ENi-C1 JIS DFCNi – Tianqiao, The product will supply to all over the world, such as: Mombasa, Swaziland, Casablanca, Many years of work experience, we have realized the importance of providing good quality products and the best before-sales and after-sales services. Most problems between suppliers and clients are due to poor communication. Culturally, suppliers can be reluctant to question things they do not understand. We break down those barriers to ensure you get what you want to the level you expect, when you want it. faster delivery time and the product you want is our Criterion .

  • Although we are a small company, we are also respected. Reliable quality, sincere service and good credit, we are honored to be able to work with you!
    5 Stars By Elvira from Portland - 2017.11.12 12:31
    The company can keep up with the changes in this industry market, product updates fast and the price is cheap, this is our second cooperation, it's good.
    5 Stars By Elva from Azerbaijan - 2017.09.30 16:36

    Send your message to us:

    Write your message here and send it to us

    Related Products

    Send your message to us: