Our company insists all along the quality policy of product quality is base of enterprise survival; customer satisfaction is the staring point and ending of an enterprise; persistent improvement is eternal pursuit of staff and the consistent purpose of reputation first, customer first for Best Welding Rods , Weld All Rods , 1018 Welding Rod , We hope we are able to have a pleasant partnership with businessman from all over the environment.

Hot-selling Different Welding Rods - Z308 Pure nickel cast iron electrode GB / T 10044 EZNi-1 AWS ENi-C1 JIS DFCNi – Tianqiao Detail:

APPLICATIONS:

It is suitable for the welding of thin pieces of cast iron welding and machining surfaces, such as cylinder heads, important gray cast iron engine blocks, gear boxes, and Machine Tool and soon.

CHARACTERISTICS:

THZ308 is pure nickel welding core, strong reduction of graphite type coating iron rod. It can be used in AC and DC dual purpose and is easy to operate. When welding, it is not necessary for weldment to preheat. It has good crack resistance and processability.

RECAUTIONS:

1. Before welding, the electrodes need to be baked for 1 hour with the temperature of 150±10℃ before using.
2 It can eliminate welding stress and avoid crack by hammering the welding seam.
3. In order to reduce the impurity elements in the base metal penetration weld, narrow white band width, improve crack resistance and processing properties, it should use small current welding in cast iron cold welding.

Chemical Composition of the deposited metal(the mass fraction): %

Elements	C	Si	Mn	S	Fe	Ni	The mass of other elements
Standard value	≤2.0	≤2.5	≤1.0	≤0.03	≤8.0	≥90	≤1.0

Welding reference current: (AC,DC⁺)

Electrode diameter(mm)	2.5	3.2	4.0
Welding current(A)	60-90	90-110	120-150

Welding distortion correction:

For deformation correction in hot state, mechanical correction and hammering are strictly prohibited in the range of blue brittle temperature (300℃~500℃) to avoid brittle cracks.

Pay attention to the following requirements when the flame is locally heated

It is not advisable to repeat heating at the same part to avoid changes in the metallographic structure and mechanical properties of the steel.

Do not cause repeated corrections of tension and compression in the same part.

For hardenable welded parts, watering and rapid cooling are strictly prohibited.

Welding parts that need to be annealed should be rectified before annealing to eliminate internal stress during annealing. During annealing, the welded parts must be placed steadily so as not to deform again.

The flame straightening heating temperature can be 700℃~850℃ (fuchsia), and should not exceed 900℃ (bright red) for low alloy structural steel.

Product detail pictures:

Related Product Guide:
The composition of the welding electrode

We insist on offering high-quality creation with superior business enterprise concept, honest revenue plus the greatest and fast service. it will bring you not only the high quality solution and huge profit, but essentially the most significant is usually to occupy the endless market for Hot-selling Different Welding Rods - Z308 Pure nickel cast iron electrode GB / T 10044 EZNi-1 AWS ENi-C1 JIS DFCNi – Tianqiao, The product will supply to all over the world, such as: Mexico, Czech Republic, Croatia, During in 11 years, We have participated in more than 20 exhibitions, obtains the highest praise from each customer. Our company has been devoting that customer first and committed to helping customers expand their business, so that they become the Big Boss !