APPLICATIONS:
It is suitable for the welding of thin pieces of cast iron welding and machining surfaces, such as cylinder heads, important gray cast iron engine blocks, gear boxes, and Machine Tool and soon.
CHARACTERISTICS:
THZ308 is pure nickel welding core, strong reduction of graphite type coating iron rod. It can be used in AC and DC dual purpose and is easy to operate. When welding, it is not necessary for weldment to preheat. It has good crack resistance and processability.
RECAUTIONS:
1. Before welding, the electrodes need to be baked for 1 hour with the temperature of 150±10℃ before using.
2 It can eliminate welding stress and avoid crack by hammering the welding seam.
3. In order to reduce the impurity elements in the base metal penetration weld, narrow white band width, improve crack resistance and processing properties, it should use small current welding in cast iron cold welding.
Chemical Composition of the deposited metal(the mass fraction): %
|
Elements |
C |
Si |
Mn |
S |
Fe |
Ni |
The mass of other elements |
|
Standard value |
≤2.0 |
≤2.5 |
≤1.0 |
≤0.03 |
≤8.0 |
≥90 |
≤1.0 |
Welding reference current: (AC,DC+)
|
Electrode diameter(mm) |
2.5 |
3.2 |
4.0 |
|
Welding current(A) |
60-90 |
90-110 |
120-150 |
Welding distortion correction:
For deformation correction in hot state, mechanical correction and hammering are strictly prohibited in the range of blue brittle temperature (300℃~500℃) to avoid brittle cracks.
Pay attention to the following requirements when the flame is locally heated
It is not advisable to repeat heating at the same part to avoid changes in the metallographic structure and mechanical properties of the steel.
Do not cause repeated corrections of tension and compression in the same part.
For hardenable welded parts, watering and rapid cooling are strictly prohibited.
Welding parts that need to be annealed should be rectified before annealing to eliminate internal stress during annealing. During annealing, the welded parts must be placed steadily so as not to deform again.
The flame straightening heating temperature can be 700℃~850℃ (fuchsia), and should not exceed 900℃ (bright red) for low alloy structural steel.
Product detail pictures:
Related Product Guide:
The composition of the welding electrode
High quality Very first,and Shopper Supreme is our guideline to offer the most beneficial company to our clients.Nowadays, we're hoping our best to be certainly one of the top exporters in our area to satisfy consumers additional will need for Professional Design 316 Stainless Welding Rod - Z308 Pure nickel cast iron electrode GB / T 10044 EZNi-1 AWS ENi-C1 JIS DFCNi – Tianqiao, The product will supply to all over the world, such as: Palestine, South Korea, Mecca, Based on experienced engineers, all orders for drawing-based or sample-based processing are welcomed. We have won a good reputation for outstanding customer service among our overseas customers. We will continue to try the best to offer you good quality products and the best service. We are looking forward to serving you.
By Louise from Wellington - 2017.06.29 18:55
We have been cooperated with this company for many years, the company always ensure timely delivery ,good quality and correct number, we are good partners.
By Ada from Czech republic - 2017.09.09 10:18